Back to Journals » International Journal of Nanomedicine » Volume 7

Ultrasmall superparamagnetic iron oxide (USPIO)-based liposomes as magnetic resonance imaging probes

Authors Frascione, Diwoky, Almer, Opriessnig, Vonach, Gradauer, Leitinger G, Mangge, Stollberger, Prassl R

Received 6 February 2012

Accepted for publication 3 March 2012

Published 9 May 2012 Volume 2012:7 Pages 2349—2359


Review by Single anonymous peer review

Peer reviewer comments 3

Daniela Frascione,1 Clemens Diwoky,2 Gunter Almer,1,3 Peter Opriessnig,2 Caroline Vonach,1 Kerstin Gradauer,1 Gerd Leitinger,4 Harald Mangge,3 Rudolf Stollberger,2 Ruth Prassl1,5

1Institute of Biophysics and Nanosystems Research, Austrian Academy of Sciences, Graz, Austria; 2Institute of Medical Engineering, University of Technology, Graz, Austria; 3Clinical Institute for Medical and Chemical Laboratory Diagnosis (CIMCL), Medical University, Graz, Austria; 4Institute of Cell Biology, Histology and Embryology, Medical University, Graz, Austria; 5Ludwig Boltzmann Institute for Lung Vascular Research, Graz, Austria

Background: Magnetic liposomes (MLs) are phospholipid vesicles that encapsulate magnetic and/or paramagnetic nanoparticles. They are applied as contrast agents for magnetic resonance imaging (MRI). MLs have an advantage over free magnetic nanocores, in that various functional groups can be attached to the surface of liposomes for ligand-specific targeting. We have synthesized PEG-coated sterically-stabilized magnetic liposomes (sMLs) containing ultrasmall superparamagnetic iron oxides (USPIOs) with the aim of generating stable liposomal carriers equipped with a high payload of USPIOs for enhanced MRI contrast.
Methods: Regarding iron oxide nanoparticles, we have applied two different commercially available surface-coated USPIOs; sMLs synthesized and loaded with USPIOs were compared in terms of magnetization and colloidal stability. The average diameter size, morphology, phospholipid membrane fluidity, and the iron content of the sMLs were determined by dynamic light scattering (DLS), transmission electron microscopy (TEM), fluorescence polarization, and absorption spectroscopy, respectively. A colorimetric assay using potassium thiocyanate (KSCN) was performed to evaluate the encapsulation efficiency (EE%) to express the amount of iron enclosed into a liposome. Subsequently, MRI measurements were carried out in vitro in agarose gel phantoms to evaluate the signal enhancement on T1- and T2-weighted sequences of sMLs. To monitor the biodistribution and the clearance of the particles over time in vivo, sMLs were injected in wild type mice.
Results: DLS revealed a mean particle diameter of sMLs in the range between 100 and 200 nm, as confirmed by TEM. An effective iron oxide loading was achieved just for one type of USPIO, with an EE% between 74% and 92%, depending on the initial Fe concentration (being higher for lower amounts of Fe). MRI measurements demonstrated the applicability of these nanostructures as MRI probes.
Conclusion: Our results show that the development of sMLs is strictly dependent on the physicochemical characteristics of the nanocores. Once established, sMLs can be further modified to enable noninvasive targeted molecular imaging.

Keywords: magnetic liposomes, fluorescence polarization, biodistribution, MRI contrast agent


Creative Commons License © 2012 The Author(s). This work is published and licensed by Dove Medical Press Limited. The full terms of this license are available at and incorporate the Creative Commons Attribution - Non Commercial (unported, v3.0) License. By accessing the work you hereby accept the Terms. Non-commercial uses of the work are permitted without any further permission from Dove Medical Press Limited, provided the work is properly attributed. For permission for commercial use of this work, please see paragraphs 4.2 and 5 of our Terms.