Back to Journals » International Journal of Nanomedicine » Volume 7

Fabrication and in vitro release behavior of a novel antibacterial coating containing halogenated furanone-loaded poly(L-lactic acid) nanoparticles on microarc-oxidized titanium

Authors Cheng Y, Wu J, Gao B, Zhao X, Yao J, Mei S, Zhang L, Ren H

Received 15 August 2012

Accepted for publication 27 September 2012

Published 7 November 2012 Volume 2012:7 Pages 5641—5652


Checked for plagiarism Yes

Review by Single anonymous peer review

Peer reviewer comments 4

Yicheng Cheng,1 Jiang Wu,1 Bo Gao,1 Xianghui Zhao,2 Junyan Yao,3 Shenglin Mei,1 Liang Zhang,4 Huifang Ren1

1Department of Prosthodontics, School of Stomatology, Fourth Military Medical University, 2Institute of Neuroscience, School of Basic Medicine, Fourth Military Medical University, 3Department of Applied Chemistry, School of Science, Northwestern Polytechnical University, 4Department of Orthodontics, School of Stomatology, Fourth Military Medical University, Xi'an, China

Yicheng Cheng and Jiang Wu contributed equally to this work

Background: Dental implants have become increasingly common for the management of missing teeth. However, peri-implant infection remains a problem, is usually difficult to treat, and may lead eventually to dental implant failure. The aim of this study was to fabricate a novel antibacterial coating containing a halogenated furanone compound, ie, (Z-)-4-bromo-5-(bromomethylene)-2(5H)-furanone (BBF)-loaded poly(L-lactic acid) (PLLA) nanoparticles on microarc-oxidized titanium and to evaluate its release behavior in vitro.
Methods: BBF-loaded PLLA nanoparticles were prepared using the emulsion solvent-evaporation method, and the antibacterial coating was fabricated by cross-linking BBF-loaded PLLA nanoparticles with gelatin on microarc-oxidized titanium.
Results: The BBF-loaded PLLA nanoparticles had a small particle size (408 ± 14 nm), a low polydispersity index (0.140 ± 0.008), a high encapsulation efficiency (72.44% ± 1.27%), and a fine spherical shape with a smooth surface. The morphology of the fabricated antibacterial coating showed that the BBF-loaded PLLA nanoparticles were well distributed in the pores of the microarc oxidation coating, and were cross-linked with each other and the wall pores by gelatin. The release study indicated that the antibacterial coating could achieve sustained release of BBF for 60 days, with a slight initial burst release during the first 4 hours.
Conclusion: The novel antibacterial coating fabricated in this study is a potentially promising method for prevention of early peri-implant infection.

Keywords: antibacterial, coating, halogenated furanone, nanoparticles, microarc oxidation, sustained release

Creative Commons License © 2012 The Author(s). This work is published and licensed by Dove Medical Press Limited. The full terms of this license are available at and incorporate the Creative Commons Attribution - Non Commercial (unported, v3.0) License. By accessing the work you hereby accept the Terms. Non-commercial uses of the work are permitted without any further permission from Dove Medical Press Limited, provided the work is properly attributed. For permission for commercial use of this work, please see paragraphs 4.2 and 5 of our Terms.