Influence of light curing and sample thickness on microhardness of a composite resin

Authors Aguiar FHB , Andrade K, Lima D, Ambrosano G, Lovadino J

Published 6 May 2009 Volume 2009:1 Pages 21—25


Review by Single anonymous peer review

Peer reviewer comments 6

Flávio HB Aguiar1, Kelly RM Andrade1, Débora AN Leite Lima1, Gláucia MB Ambrosano2, José R Lovadino1

1Department of Restorative Dentistry; 2Department of Social Dentistry/Statistics, Piracicaba Dental School, State University of Campinas, SP, Brazil

Abstract: The aim of this in vitro study was to evaluate the influence of light-curing units and different sample thicknesses on the microhardness of a composite resin. Composite resin specimens were randomly prepared and assigned to nine experimental groups (n = 5): considering three light-curing units (conventional quartz tungsten halogen [QTH]: 550 mW/cm2 – 20 s; high irradiance QTH: 1160 mW/cm2 – 10 s; and light-emitting diode [LED]: 360 mW/cm2 – 40 s) and three sample thicknesses (0.5 mm, 1 mm, and 2 mm). All samples were polymerized with the light tip 8 mm away from the specimen. Knoop microhardness was then measured on the top and bottom surfaces of each sample. The top surfaces, with some exceptions, were almost similar; however, in relation to the bottom surfaces, statistical differences were found between curing units and thicknesses. In all experimental groups, the 0.5-mm-thick increments showed microhardness values statistically higher than those observed for 1- and -2-mm increments. The conventional and LED units showed higher hardness mean values and were statistically different from the high irradiance unit. In all experimental groups, microhardness mean values obtained for the top surface were higher than those observed for the bottom surface. In conclusion, higher levels of irradiance or thinner increments would help improve hybrid composite resin polymerization.

Keywords: photo-polymerization, light-curing distance, light-curing units, composite resin, composite thickness, microhardness

Creative Commons License This work is published and licensed by Dove Medical Press Limited. The full terms of this license are available at and incorporate the Creative Commons Attribution - Non Commercial (unported, v3.0) License. By accessing the work you hereby accept the Terms. Non-commercial uses of the work are permitted without any further permission from Dove Medical Press Limited, provided the work is properly attributed. For permission for commercial use of this work, please see paragraphs 4.2 and 5 of our Terms.